| Property | Test Standard | Test Condition | Unit | Typical Value |
|---|---|---|---|---|
| Specific Gravity | ISO 1183 | 23°C | g/cm³ | 1.15 |
| Shrinkage Rate – Flow | ISO 2577 | 23°C | % | 0.4–0.6 |
| Melt Index | ISO 1133 | 230°C / 5 kg | g/10 min* | 8 |
| Rockwell Hardness | ISO 2039 | R Scale | — | 101 |
| Tensile Strength | ISO 527 | 50 mm/min | MPa | 23 |
| Elongation at Break | ISO 527 | 50 mm/min | % | 30 |
| Flexural Strength | ISO 178 | 2.0 mm/min | MPa | 35 |
| Flexural Modulus | ISO 178 | 2.0 mm/min | MPa | 2,000 |
| Notched Impact Strength | ISO 180 | 23°C, A-notch | kJ/m² | 8.0 |
| H.D.T. | ISO 75 | 0.45 MPa | °C | 81 |
| H.D.T. | ISO 75 | 1.8 MPa | °C | 72 |
| Thermal Deformation Temperature | ISO 306 | 0.45 MPa | °C | 94 |
| Vicat Softening Temperature | ISO 306 | 1.8 MPa | °C | 85 |
| Volume Resistivity | IEC 60093 | — | Ω·cm | 1 × 10¹⁶ |
| Dielectric Strength | IEC 60243 | — | kV/mm | 22 |